LEXAN™
FXD941A resin
聚碳酸酯
SABIC
Innovative Plastics
产品说明:
FXD153 is an Extrusion / Blow molding grade in a Diffusion effect,
which is part of the VisualFX family. These effects have been developed to meet
increasing Aesthetic demands in the Marketplace. Color Package may affect
properties, Application testing always reccomended.
| 总体 | ||||
|
材料状态
|
|
|||
|
资料 1
|
|
|||
|
搜索 UL
黄卡
|
|
|||
|
供货地区
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
1.20
|
g/cm³
|
ASTM D792 |
|
熔流率（熔体流动速率） (300°C/1.2
kg)
|
2.5
|
g/10 min
|
ASTM D1238 |
|
收缩率 - 流动 (3.20 mm)
|
0.50 到 0.70
|
%
|
内部方法 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量 2
|
2340
|
MPa
|
ASTM D638 |
|
抗张强度 3
|
ASTM D638 | ||
|
屈服
|
62.0
|
MPa
|
|
|
断裂
|
66.0
|
MPa
|
|
|
伸长率 3
|
ASTM D638 | ||
|
屈服
|
7.0
|
%
|
|
|
断裂
|
110
|
%
|
|
|
弯曲模量 4 (50.0 mm 跨距)
|
2340
|
MPa
|
ASTM D790 |
|
弯曲强度 4 (屈服, 50.0 mm
跨距)
|
93.0
|
MPa
|
ASTM D790 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
悬壁梁缺口冲击强度 (23°C)
|
750
|
J/m
|
ASTM D256 |
|
无缺口悬臂梁冲击 (23°C)
|
3200
|
J/m
|
ASTM D4812 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
载荷下热变形温度
|
ASTM D648 | ||
|
0.45 MPa,
未退火, 3.20 mm
|
138
|
°C
|
|
|
1.8 MPa,
未退火, 3.20 mm
|
132
|
°C
|
|
|
维卡软化温度
|
157
|
°C
|
ASTM D1525 5 |
|
线形热膨胀系数 - 横向 (-40 到 40°C)
|
6.8E-5
|
cm/cm/°C
|
ASTM E831 |
| 注射 |
额定值
|
单位制
|
|
|
干燥温度
|
121
|
°C
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
干燥时间，最大
|
48
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 60
|
%
|
|
|
料筒后部温度
|
299 到 321
|
°C
|
|
|
料筒中部温度
|
310 到 332
|
°C
|
|
|
料筒前部温度
|
321 到 343
|
°C
|
|
|
射嘴温度
|
316 到 338
|
°C
|
|
|
加工（熔体）温度
|
321 到 343
|
°C
|
|
|
模具温度
|
82.2 到 116
|
°C
|
|
|
背压
|
0.345 到 0.689
|
MPa
|
|
|
螺杆转速
|
40 到 70
|
rpm
|
|
|
排气孔深度
|
0.025 到 0.076
|
mm
|
| 备注 |
| 1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。 |
| 25.0 mm/min |
| 3类型 1, 50 mm/min |
| 41.3 mm/min |
| 5标准 B (120°C/h), 载荷2 (50N) |